FALCON (Brazing Rods) Cadmium free silver brazing alloy. The only flux coated silver flux strong enough to clean oxidized stainless steel. No odors from rubberized compounds yet the flux coating is totally flexible and non-fragile. APPLICATIONS: Low temperature joining of dissimilar met als - including stainless steel, brass and copper. Excellent where tolerances and fit are not perfect. Special “Fast Flow” flux coating provides twice the base metal cleansing action of conventional silver flux coatings. Cadmium free rod can be used in the food, medical & pharmaceutical industries. WELDING TECHNIQUES: After cleaning metal, preheat generally to 350°F (200°C) then heat the joint area to 800°F (420°C). Melt off some flux and allow it to flow throughout the joint. Then add alloy. TEMPERATURE RANGES: Working Temperature: 1245°F (674°C) Melting Range: 1175°F (639°C) Solidus 1235°F (670°C) Liquidus 4 DEFENSE (Brazing Rods) Bronze brazing alloy with slick, smooth moisture sealed flux has triple the shelf life of similar products. Flux cleansing action is exceptional on dirty steels and cast irons. APPLICATIONS: Torch brazing most steels and cast irons. Especially suited for joining thin sections. Unique “Safe Vue” flux coating eliminates harsh chemical odors and the bright orange visibility blocking glare of conventional sodium type flux coatings. WELDING TECHNIQUES: Insure that parts to be joined are clean. Pre-heat general area to 700°F (400°C) and then specific area to 1200°F (650°C). Melt off flux and apply alloy. TEMPERATURE RANGES: Working Temperature: 1595°F (878°C) Melting Range: TORCH SETTING: Slightly carburizing TYPICAL MECHANICAL PROPERTIES: Undiluted Weld Metal Maximum Value Up To 68,000 psi (465 N/mm 2 ) 54,000 psi (372 N/mm 2 ) Tensile strength Yield strength Elongation Hardness 25% Brinell 120 DIAMETER PART LENGTH RODS PER (INCHES) NUMBER (INCHES) 1/4 POUND 1/16 3/32 818301 818303 18 18 8

ARMOR (Brazing Rods) Ultra high purity nickel silver alloy. Slick, smooth moisture sealed flux has triple the shelf life of similar products. Exceptional on dirty steels and cast irons. APPLICATIONS: High strength joining of steels using the thin flow and bead form techniques. Unique “Safe Vue” flux coating eliminates harsh chemical odors and the bright orange visibility blocking glare of conventional sodium type flux coatings. WELDING TECHNIQUES: Insure that parts to be joined are clean. Pre-heat general area to 700°F (400°C) and then spe cific area to 1200°F (650°C). Melt off flux and apply alloy. TEMPERATURE RANGES: Working Temperature: 1595°F (878°C) Melting Range:

1583° - 1640°F (870° - 895°C)

D11 D12 D13 D14

TORCH SETTING: Neutral flame. TYPICAL MECHANICAL PROPERTIES: Undiluted Weld Metal

Maximum Value Up To 102,000 psi (700 N/mm 2 ) 90,000 psi (630 N/mm 2 )

Tensile strength Yield strength

Elongation Hardness

28%

Rockwell B 96 Brinell 210 Rockwell C 25 Brinell 265

Work Hardness

DIAMETER PART

LENGTH RODS PER

(INCHES)

NUMBER (INCHES)

POUND

3/32

18

23

818323

ALADDIN 3 IN 1 ROD

• WELD • BR A ZE • SOLDER • N o Flux Required Repairs all...aluminum and zinc alloys quick and easily

For use with acetylene, propane and mapp gas

Use To Repair: Kirksite dies, power tools, aluminum radiators, propellers, castings, lower units, hardware accessories, boat hulls.

NO FLUX REQUIRED for ... • WELDING zinc-base metals. • BRAZING aluminum. • SOLDERING galvanized metal. • High-quality virgin metal. Meets Mil Spec: MIL-R-4208 Melting Point: 732° F

• Sold in one pound tubes. • 18 inch length.

1583° - 1620°F (870° - 885°C)

TORCH SETTING: Neutral flame.

TYPICAL MECHANICAL PROPERTIES: Undiluted Weld Metal

Maximum Value Up To 71,000 psi (490 N/mm 2 ) 64,000 psi (440 N/mm 2 )

Tensile strength Yield strength

Part No. 818001 Assortment Package Includes: (1) 1/4”, (2) 3/16”, (3) 5/32”, (4) 3/32”, (5) 1/16” (Bal.) 1/8” Diameters

Elongation

27%

DIAMETER PART

LENGTH RODS PER

(INCHES)

NUMBER (INCHES)

POUND

3/32 1/8

18 18

23 13

818313 818314

PSS072514

D13-5 REVISED MARCH, 2016

© Copyright 2026. All rights reserved. No portion may be copied or reproduced in any manner.